Fiber-reinforced polymer composition and method of producing same

ABSTRACT

Fiber-reinforced polymer compositions containing resin components including (a) 30-90 weight % of polyamide resins, and (b) 10-70 weight % of polyolefins+unsaturated carboxylic acid-modified polyolefins, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the total compositions, a molar ratio of end amino groups in the polyamide resins to carboxyl groups in the modified polyolefins being 10-1000. The compositions have a morphology in which polyolefin domains having an average size of 0.5-5 μm are uniformly dispersed in polyamide matrix phases. They are produced by a double-screw extruder having a length/inner diameter (L/D) ratio of 25 or more and having a first hopper for introducing the resin components, a second hopper for introducing the glass fibers, a vent and a die exit in this order, and further having at least one first kneading zone for strongly kneading the resin components, and at least one second kneading zone disposed between the second hopper and the vent for strongly kneading the resin components and the glass fibers.

BACKGROUND OF THE INVENTION

The present invention relates to fiber-reinforced polymer compositions comprising polyamide resins and polyolefins as main components, and more particularly to fiber-reinforced polymer compositions comprising polyamide resins and polyolefins as main components, which have excellent thermal deformation resistance, chemical resistance, impact resistance, antifreeze resistance, water absorption resistance and moldability, and further remarkably improved tensile strength, flexural modulus, creep resistance, etc. depending upon their additives.

Containers such as radiator tanks of automobiles are increasingly produced from plastics, for the purpose of reducing their weight. As plastic materials for producing such containers, polyamide resins are highly suitable because they are light and excellent in impact resistance, heat resistance, chemical resistance, etc. Particularly, nylon 6 and nylon 66 having excellent strength and when heat resistance and blended with glass fibers are widely used.

However, despite the fact that polyamide resins reinforced with glass fibers, etc. are excellent in heat resistance, mechanical strength and long-term durability, they are generally poor in water resistance, moldability, chemical resistance and antifreeze resistance. Particularly, the antifreeze resistance is an important characteristic when they are used for radiator tanks of automobiles.

The above desired properties, which are insufficient in the polyamide resins, are generally present in polyolefins. Thus, various compositions based on polyamide resins, polyolefins and glass fibers have been proposed.

Japanese Patent Publication No. 61-26939 discloses radiator tanks made of compositions comprising (a) polyamide resins, (b) modified polymers obtained by grafting ethylenically unsaturated carboxylic acids or their anhydrides to polypropylene resins, and (c) fibrous reinforcing materials, a weight ratio of the component (a) to the component (b) being 70:30-95:5 and the component (c) being 40-200 parts by weight per 100 parts by weight of the total amount of the component (a) and the component (b).

Japanese Patent Laid-Open No. 61-76540 discloses molded plastic articles for automobiles having one surface exposed to the atmosphere and the other surface exposed to water and being repeatedly subjected to high temperature, the molded articles being made of (A) 90-10 parts by weight of olefin polymers, (B) 10-90 parts by weight of polyamides, and (C) 0.1-20 parts by weight, per 100 parts by weight of (A)+(B), of modified olefin polymers grafted with 0.05-10 parts by weight of monomers selected from unsaturated carboxylic acids or their derivatives.

Japanese Patent Laid-Open No. 62-241940 discloses plastic compositions for radiator tanks for automobiles comprising (A) 30-95 weight % of olefin polymers (B) 5-70 weight % of polyamides, and (C) 5-200 parts by weight, per 100 parts by weight of (A)+(B), of glass fibers impregnated with acrylic resins as tying agents.

These polyamide compositions may be produced by any known methods, for instance, by methods using a Henschel mixer, a V-blender, a single-screw extruder, a vented extruder, a double-screw extruder, a kneader, etc.

However, despite the fact that in the conventional compositions, the compatibility of polyamide resins and polyolefins and the adhesion of glass fibers to the matrix resins are improved, they are still insufficient for severe conditions required for radiator tanks, etc.

Further, since the polyolefin components are vulnerable to C-C chain scission when exposed at high temperature, resulting in the deterioration of their mechanical properties, it is desired to prevent the oxidation deterioration of the compositions at high temperature as part materials used in a high-temperature environment near engines.

In addition, since polyolefins have relatively high brittle temperatures, it is desired to improve the low-temperature impact resistance of their compositions.

OBJECT AND SUMMARY OF THE INVENTION

An object of the present invention is, therefore, to provide fiber-reinforced polymer compositions having excellent water resistance, moldability and antifreeze resistance owned by polyolefins while retaining excellent properties such as thermal deformation resistance of the polyamide resins, desirably with such properties further improved.

Another object of the present invention is to provide fiber-reinforced polymer compositions further provided with thermal deterioration resistance and low-temperature impact resistance in addition to the above properties.

A further object of the present invention is to provide fiber-reinforced polymer compositions having improved bonding strength between glass fibers and matrix resins.

A still further object of the present invention is to provide fiber-reinforced polymer compositions provided with remarkably improved impact resistance and flexural modulus.

A still further object of the present invention is to provide fiber-reinforced polymer compositions provided with remarkably improved heat resistance and creep resistance.

A still further object of the present invention is to provide fiber-reinforced polymer compositions provided with remarkably improved moldability, antifreeze resistance, chemical resistance and water resistance.

A still further object of the present invention is to provide a method and an apparatus for industrially and stably producing such fiber-reinforced polymer compositions with improved properties.

As a result of intense research in view of the above objects, the inventors have found that the fiber-reinforced polymer compositions with the above improved properties can be obtained by adding unsaturated carboxylic acid-modified polyolefins to polyamide resins, polyolefins and glass fibers.

It has also been found that by selecting a molar ratio of end amino groups of polyamide resins to carboxyl groups of modified polyolefins by the addition of a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers, the compatibility between polyamide resins and polyolefins is considerably improved, thus providing fiber-reinforced polymer compositions having excellent properties peculiar to both components.

It has further been found that by forming a particular morphology in which fine polyolefin domain phases are uniformly dispersed in a polyamide resin matrix phase by the addition of unsaturated carboxylic acid-modified polyolefins to polyamide resins, polyolefins and glass fibers, the fiber-reinforced polymer compositions can exhibit water resistance moldability and antifreeze resistance peculiar in polyolefins at maximum levels while retaining thermal deformation resistance of the polyamide resins.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers, but also by treating the glass fibers with particular tying agents and coupling agents, improved bonding strength between the glass fibers and matrix resins can be achieved, thereby providing the resulting fiber-reinforced polymer compositions with improved properties.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers but also by adding inorganic fillers in the form of a sphere, flake or fine fiber such as talc, mica, potassium titanate, etc., the resulting fiber-reinforced polymer compositions can be provided with further improved mechanical properties.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers, but also by adding nucleating agents thereto, the resulting fiber-reinforced polymer compositions can be provided with remarkably improved impact resistance and modulus.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers, but also by using, as polyamide resins, nylon 66 and nylon 6 at a nylon 66/nylon 6 weight ratio of 40/60-90/10, the crystallinities of polyamide resins are reduced, and their compatibility with polyolefins is improved, thereby providing the resulting fiber-reinforced polymer compositions with remarkably improved ductility and impact resistance.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers but also by using nylon 46 as a polyamide resin, the resulting fiber-reinforced polymer compositions can be provided with remarkably improved heat resistance, mechanical strength and creep resistance.

Further, it has been found that not only by adding a proper amount of unsaturated carboxylic acid-modified polyolefins to compositions of polyamide resins, polyolefins and glass fibers, but also by using the polyamide resins including nylon 12, nylon 612 or nylon 11, the resulting fiber-reinforced polymer compositions can be provided with further improved antifreeze resistance, chemical resistance, moldability and water absorption resistance.

Further, it has been found that by using a double-screw extruder having a hopper for introducing resin components of polyamide resins and polyolefins and a hopper for introducing glass fibers and a vent, and by providing the extruder with a first kneading zone for blending the resin components and a second kneading zone for blending the resin components with the glass fibers to achieve sufficient blending, it is possible to produce fiber-reinforced polymer compositions exhibiting water resistance, moldability and antifreeze resistance peculiar in polyolefins at maximum levels while retaining the thermal deformation resistance of the polyamide resins, and the resulting compositions can be stably pelletized by extrusion.

Thus, the fiber-reinforced polymer composition according to one embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition.

The fiber-reinforced polymer composition according to another embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition, a molar ratio of end amino groups in the polyamide resin to carboxyl groups in the unsaturated carboxylic acid-modified polyolefin being 10-1000.

The fiber-reinforced polymer composition according to a further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition, the polyamide resin constituting a continuous matrix phase, and the polyolefin constituting uniformly dispersed domain phases having an average size of 0.5-5 μm.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight, per 100 parts by weight of the entire composition, of glass fibers coated with a silane coupling agent and a tying agent made of a carboxyl group- or acid anhydride group-containing polymer.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b)10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers, and (d) 1-10 parts by weight of a spherical, flaky or fibrous inorganic filler, per 100 parts by weight of the entire composition.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and, per 100 parts by weight of the entire composition, (c) 5-50 parts by weight of glass fibers, and (d) 0.03-3 parts by weight of at least one nucleating agent selected from the group consisting of:

(1) a metal salt of aromatic carboxylic acid;

(2) a metal salt of an alkyl group-substituted derivative of aromatic carboxylic acid; and

(3) dibenzylidene sorbitol.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition; characterized in that the polyamide resin consists of nylon 66 and nylon 6 in a proportion (weight ratio) of 40/60-90/10.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b)10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition; characterized in that the polyamide resin consists of nylon 46.

The fiber-reinforced polymer composition according to a still further embodiment of the present invention comprises resin components comprising (a) 30-90 weight % of a polyamide resin, and (b) 10-70 weight % of polyolefin+unsaturated carboxylic acid-modified polyolefin, based on the resin components; and (c) 5-50 parts by weight of glass fibers per 100 parts by weight of the entire composition; characterized in that the polyamide resin consists of nylon 12, nylon 612 or nylon 11.

The method of producing a fiber-reinforced polymer composition according to the present invention comprises using a double-screw extruder having a first hopper, a second hopper, a vent and a die exit in this order and having a length/inner diameter (L/D) ratio of 25 or more; introducing resin components containing the polyamide resin the polyolefin and the unsaturated carboxylic acid-modified polyolefin into the double-screw extruder through the first hopper; strongly kneading the resin components in at least one first kneading zone constituted by four or more continuously arranged kneading discs before reaching the second hopper; keeping the temperature of the resin components at 290°-320° C. on the upstream side of the second hopper; introducing the glass fibers through the second hopper; and strongly kneading the resin components with the glass fibers in at least one second kneading zone constituted by four or more continuously arranged kneading discs before reaching the vent.

The double-screw extruder for producing a fiber-reinforced polymer composition according to the present invention has a length/inner diameter (L/D) ratio of 25 or more, and comprises a first hopper for introducing resin components containing the polyamide resin, the polyolefin and the unsaturated carboxylic acid-modified polyolefin, a second hopper for introducing the glass fibers, a vent and a die exit in this order, and further comprises at least one first kneading zone located upstream of the second hopper and constituted by four or more continuously arranged kneading discs for strongly kneading the resin components, and at least one second kneading zone located between the second hopper and the vent and constituted by four or more continuously arranged kneading discs for strongly kneading the resin components and the glass fibers.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a partially cross-sectional schematic side view showing one example of a double-screw extruder for producing the fiber-reinforced polymer composition according to the present invention;

FIG. 2 is a partial enlarged view showing a kneading zone of the double-screw extruder used in the method of the present invention; and

FIG. 3 is a cross-sectional view showing one example of a pair of kneading discs.

DETAILED DESCRIPTION OF THE INVENTION

The polyamide resins which may be used in the present invention include polyamide resins formed from aliphatic, alicylic or aromatic diamines such as hexamethylenediamine, decamethylenediamine, dodecamethylenediamine, 2,2,4- or 2,4,4-trimethylhexamethylenediamine, 1,3- or 1,4-bis (aminomethyl) cyclohexane, bis (p-aminocyclohexylmethane), m- or p-xylylenediamine, etc., and aliphatic, alicyclic or aromatic dicarboxylic acids such as adipic acid, suberic acid, sebacic acid, cyclohexane carboxylic acid, telephthalic acid, isophthalic acid, etc.; polyamide resins formed from amino carboxylic acids such as 6-amino caproic acid, 11-amino undecanoic acid, 12-amino dodecanoic acid, etc.; polyamide resins formed from lactams such as ε-caprolactam, ω-dodecalactam, etc.; polyamide copolymers made of these components; and mixtures of these polyamide resins. Specifically, the polyamide resins may be nylon 6, nylon 66, nylon 610, nylon 9, nylon 6/66, nylon 66/610, nylon 6/11, etc. Among them, nylon 6 and nylon 66 are particularly preferable from the aspect of good rigidity and heat resistance.

The molecular weights of the polyamide resins are not particularly restricted, but it is preferable to use the polyamide resins with relative viscosities η_(r) (measured in 98% sulfuric acid, JIS K6810) of 1.0 or more. Particularly those having relative viscosities of 2.0 or more are preferable because of their excellent mechanical strength.

In the present invention, the particularly preferred polyamide resins are a combination of nylon 66 and nylon 6, having a nylon 66/nylon 6 weight ratio of 40/60-90/10. When the above weight ratio is lower than 40/60, the compositions show poor antifreeze resistance, and when it exceeds 90/10, the compositions show insufficient impact strength. The preferred weight ratio of nylon 66 to nylon 6 is 50/50-80/20.

Another preferred polyamide resin is nylon 46 in the present invention. Nylon 46 is polyamide obtained from diaminobutane and adipic acid, having repeating units of (CH₂)₄ connected via amide bonds. In the present invention, nylon 46 can be used alone as the polyamide resin, but, if necessary, part of nylon 46 may be substituted by nylon 66 and/or nylon 6. When nylon 66 and/or nylon 6 are contained, their total amount is 85 parts by weight or less per 100 parts by weight of the entire polyamide resin. When the total amount of nylon 66 and/or nylon 6 exceeds 85 parts by weight, the resulting compositions show poor heat resistance, mechanical strength and creep resistance. The preferred amount of nylon 66 and/or nylon 6 is 50 parts by weight or less.

Besides them, additional preferable polyamide resins used in the present invention are nylon 12, nylon 612 and nylon 11. They may be used alone or in combination. In this case, the polyamide resin may further contain 85 parts by weight or less of nylon 66 and/or nylon 6 per 100 parts by weight of the polyamide resin. When nylon 66 and/or nylon 6 exceeds 85 parts by weight, the resulting compositions show poor antifreeze resistance, chemical resistance, and water absorption resistance. The preferred amount of nylon 66 and/or nylon 6 contained in the polyamide resins (at least one of nylon 12, nylon 612 and nylon 11) is 50 parts by weight or less.

The polyolefins which may be used in the present invention include homopolymers of α-olefins such as ethylene, propylene, butene-1, pentene-1, hexene-1, 4-methylpentene-1, etc.; copolymers of ethylene and propylene or other α-olefins; and copolymers of these α-olefins. Among them, various types of polyethylene such as low-density polyethylene, linear low-density polyethylene, medium-density polyethylene and high-density polyethylene, and polypropylene are preferable. When propylene is used, it is not restricted to a homopolymer of propylene, and any random or block copolymers of propylene and other α-olefins, in which the propylene content is 50 mol % or more and preferably 80 mol % or more, may be used. The comonomers copolymerizable with propylene are ethylene and other α-olefins, and ethylene is particularly preferable. Accordingly, the term "polypropylene" used herein means that it is not restricted to a homopolymer of propylene but it includes any types of propylene copolymers.

The modified polyolefins which may be used in the present invention mean polyolefins modified with unsaturated carboxylic acids or their anhydrides. The unsaturated carboxylic acids or their anhydrides include monocarboxylic acids such as acrylic acid, methacrylic acid, etc.; dicarboxylic acids such as maleic acid, endomethylenetetrahydrophthalic acid, fumaric acid, itaconic acid, etc.; dicarboxylic anhydrides such as maleic anhydride, endomethylenetetrahydrophthalic anhydride, itaconic anhydride, etc., and particularly dicarboxylic acids or their anhydrides are preferable.

The polyolefins to be modified with unsaturated carboxylic acids or their derivatives are, like the above-described polyolefins, not limited to homopolymers of α-olefins but include copolymers of different α-olefins.

The content of unsaturated carboxyl acids or their anhydrides in the modified polyolefins is preferably determined such that a molar ratio of amino groups/carboxylic groups is within the range of 10-1000. Specifically it is preferably 0.01-15 weight %. When the content of the unsaturated carboxylic acids or their anhydrides grafted is less than 0.01 weight %, the addition of the modified polyolefins does not provide sufficient effect of improving the compatibility of the polyamide resins with polyolefins. On the other hand, when it exceeds 15 weight %, the modified polyolefins show poor compatibility with polyolefins.

The modified polyolefins may be produced by a solution method or a melt-blending method. In the case of a melt-blending method, polyolefins, unsaturated carboxylic acids or their anhydrides for modifying the polyolefins and catalysts are charged into an extruder, a double-screw blender, etc. and blended in a molten state at a temperature of 150°-250° C. Alternatively, in the case of a solution method, the above starting materials are dissolved in organic solvents such as xylene, and a reaction is conducted while stirring at a temperature of 80°-140° C. In any case, the catalysts may be usual radical polymerization catalysts. Specific examples of the catalysts include peroxides such as benzoyl peroxide, lauroyl peroxide, di-tert-butyl peroxide, acetyl peroxide, tert-butyl perbenzoate, dicumyl peroxide, perbenzoic acid, peracetic acid, tert-butyl perpivalate; azo compounds such as azobisisobutyronitrile, etc. The amount of catalysts added is 1-100 parts by weight or so per 100 parts by weight of the unsaturated carboxylic acids or their anhydrides.

In the fiber-reinforced polymer compositions of the present invention, the polyamide resin is 30-90 weight %, and the polyolefin+the modified polyolefin is 10-70 weight %, based on the resin components. When the polyamide resin is less than 30 weight %, the resulting compositions do not show sufficient heat resistance and mechanical strength, and when it exceeds 90 weight %, the resulting compositions do not show sufficient moldability and antifreeze resistance, and their production costs become high. The preferred amount of the polyamide resin is 55-70 weight %, and the preferred amount of the polyolefin+the modified polyolefin is 30-50 weight %.

The amount of the modified polyolefin, particularly the content of the carboxyl groups in the modified polyolefin, preferably has a close relation with the content of end amino groups in the polyamide resin. It is presumed that in the process of melt-blending, the carboxyl groups in the modified polyolefins are reacted with the end amino groups of the polyamide resins to form modified polyolefin-polyamide resin graft copolymers which serve as compatibilizing agents for the polyolefins and the polyamide resins, and that the amount of the graft copolymers formed is closely related to a molar ratio of end amino groups of the polyamide resins/carboxyl groups. Accordingly, it is preferable to adjust the amount of the modified polyolefins in the compositions such that the molar ratio of end amino groups to the carboxyl groups of the modified polyolefins is within the range of 10-1000. When the amino group/carboxyl group molar ratio is less than 10, too much compatibility is obtained, thereby reducing the heat resistance of the resulting compositions because the properties of the polyamide resins and the polyolefins are averaged. On the other hand, when the amino group/carboxyl group molar ratio exceeds 1000, sufficient compatibilizing effect cannot be obtained by the addition of the modified polyolefins, resulting in the compositions with poor mechanical strength. More preferred molar ratio is 20-200. Incidentally, to meet the above requirements of the molar ratio, the amount of the modified polyolefins is generally 0.1-20 weight % and preferably 0.5- 10 weight %.

The amount of the glass fibers is 5-50 parts by weight per 100 parts by weight of the entire composition. When the glass fibers are less than 5 parts by weight, the resulting composition do not have sufficient heat resistance and mechanical strength. On the other hand, when they exceed 50 parts by weight, the resulting compositions show poor moldability and reduced mechanical strength. The preferred amount of glass fibers is 15-40 parts by weight. Incidentally, the glass fibers are preferably in the form of chopped strands, robing, etc. with fiber diameter of 5-15 μm.

In the present invention, the glass fibers are preferably surface-treated with (1) silane coupling agents and (2) tying agents composed of polymers having carboxyl groups or their anhydride groups. By this surface treatment, the adhesion of the glass fibers to the matrix resins, particularly polyamide resins, is improved, thereby providing the resulting compositions with drastically improved heat resistance, antifreeze resistance and mechanical properties.

The silane coupling agents which may be used in the present invention include amino silane, epoxy silane, methyltrimethoxy silane, methyltriethoxy silane, γ-glycidoxypropyltrimethoxy silane, vinyl triacetoxy silane, hexamethyl silane, vinyl trimethoxy silane, etc.

The polymers having carboxyl groups or their anhydride groups which may be used as tying agents include polymers of monocarboxylic acids such as acrylic acid, methacrylic acid etc., dicarboxylic acids such maleic acid, endomethylenetetrahydrophthalic acid, fumaric acid, itaconic acid, or dicarboxylic acid anhydrides such as maleic anhydride, endomethylenetetrahydrophthalic anhydride, itaconic anhydride, etc.; and copolymers of these carboxylic acids and vinyl compounds such as stylene, ethylene, etc. Among them, copolymers of monocarboxylic acids or dicarboxylic acids are particularly preferable.

The silane coupling agents and the tying agents may be applied to the glass fibers by immersing the glass fibers in aqueous solutions or emulsions of the silane coupling agents and the tying agents, or by spraying the above aqueous solutions or emulsions to the glass fibers. In this case, silane coupling agents and the tying agents may be applied simultaneously as a single aqueous solution or aqueous emulsion, or they may be applied separately by separate aqueous solutions or emulsions. In the case of separate application, the silane coupling agents are preferably applied first.

After applying the silane coupling agents and the tying agents by the above method, the glass fibers are preferably heated at 100°-200° C. for 1-30 minutes to accelerate the drying of the glass fibers and the hardening reaction of the silane coupling agents.

The amount of the silane coupling agents applied is preferably 0.1-1 weight % based on the glass fibers. When the amount of the silane coupling agents is less than 0.1 weight %, the glass fibers cannot be completely covered by the silane coupling agents. On the other hand, when it exceeds 1 weight %, too thick a silane coupling agent layer is formed on the glass fibers. The particularly preferred amount of the silane coupling agents applied is 0.3-0.5 weight %.

The amount of the tying agents is preferably 5-20 times that of the silane coupling agents. That is, it is preferably 1.5-10% based on the weight of the glass fibers. When the amount of the tying agents is less than 1.5 weight %, the glass fibers are not well tied, and they are not strongly adhered to the matrix resins. On the other hand, when the tying agents exceed 10 weight %, the glass fibers are not well dispersed in the process of extrusion blending.

The fiber-reinforced polymer compositions of the present invention may further contain inorganic fillers in the form of a sphere, flake or fiber, such as talc, mica, potassium titanate, etc. in an amount of 1-10 parts by weight, per 100 parts by weight of the entire composition, to improve the mechanical properties such as tensile strength, flexural modulus and impact strength. The above inorganic fillers may be a combination of two or more spherical, flaky or finely fibrous compounds such as talc, mica, potassium titanate, etc. In this case, the total amount of two or more compounds is 1-10 parts by weight. When the amount of the inorganic fillers is less than 1 part by weight, the sufficient improvement in tensile strength, flexural modulus, etc. cannot be obtained, and when it exceeds 10 parts by weight, the impact strength of the compositions decreases. The preferred amount of the inorganic fillers is 2-8 parts by weight.

The fiber-reinforced polymer compositions of the present invention may further contain at least one nucleating agent selected from the group consisting of (a), (b) and (c) in an amount of 0.03-3 parts by weight per 100 parts by weight of the entire compositions:

(a) a metal salt of aromatic carboxylic acid,

(b) a metal salt of alkyl group-substituted derivative of aromatic carboxylic acid, and

(c) dibenzylidene sorbitol.

When the amount of the above nucleating agents is less than 0.03 parts by weight, the above effects cannot be obtained. On the other hand, when the amount of the nucleating agents exceeds 3 parts by weight, further improvement of the above properties cannot be obtained, simply increasing the production costs of the compositions. The preferred amount of the nucleating agents is 0.05-1 parts by weight.

Specific examples of the compounds (a) and (b) include sodium benzoate, aluminum p-tert-butylbenzoate, titanium p-tert-butylbenzoate, chromium p-tert-butylbenzoate, aluminum monophenyl acetate, aluminum p-tert-butylmonohydroxybenzoate, etc.

The fiber-reinforced polymer compositions of the present invention has a morphology in which the polyamide resin forms a continuous matrix phase, while the polyolefin forms a domain phase having an average size of 0.5-5 μm. When the polyamide resin does not form a continuous matrix phase or when polyolefin domains have an average size of less than 0.5 μm, the resulting compositions show extremely low thermal deformation resistance. On the other hand, when the polyolefin domains have an average size exceeding 5 μm, the resulting compositions show drastically insufficient tensile strength, flexural modulus, impact strength, etc.

The fiber-reinforced polymer compositions of the present invention may further contain other additives such as thermostabilizers, anti-oxidants, photostabilizers, flame retarders, plasticizers, anti-static agents, parting agents, foaming agents, etc. to improve their properties.

The compositions of the present invention may be produced by blending in a molten state by using a single-screw extruder, a double-screw extruder, etc.

In the production of the fiber-reinforced polymer compositions of the present invention, the double-screw extruder satisfying the following requirements is preferably used:

(a) Having a first hopper, a second hopper, a vent and a die exit in this order;

(b) Having at least one first kneading zone located upstream of the second hopper for strongly blending the resin components; and

(c) Having at least one second kneading zone located between the second hopper and the vent for strongly blending the resin components and the glass fibers.

With respect to the requirement (a), the first hopper is for charging the polyamide resin, the polyolefin and the modified polyolefin into the double-screw extruder, the second hopper is for charging the glass fibers, the vent is for removing low-molecular components generated during the blending of the resin components and the glass fibers, and the die exit is for extruding the blended compositions in the form of strand.

With respect to the requirement (b), the first kneading zone is for strongly kneading the resin components, and, if necessary, a plurality of the first kneading zones are provided. Each first kneading zone is constituted by 4 or more, particularly 4-16 kneading discs arranged continuously. Each pair of the kneading discs are fixed to two screw shafts, so that they are rotated by the rotation of the screws. Since each kneading disc is in a cam shape, a gap between each pair of the kneading discs is changed by the rotation of the screws. Thus, the resin components passing therethrough are strongly blended.

With respect to the requirement (c), the second kneading zone is for strongly blending the resin components and the glass fibers, and its structure itself is essentially the same as the first kneading zone.

The double-screw extruder having the above structural features has a structure as illustrated in FIG. 1. This double-screw extruder preferably has the following structure:

(a) A length/diameter (L/D) ratio of the double-screw extruder is 25 or more;

(b) It has:

(1) A first hopper 1 for charging the resin components;

(2) Die 2 for extruding the fiber-reinforced polymer compositions;

(3) A second hopper 3 positioned in L/D 15-20 downstream of the first hopper for introducing the glass fibers;

(4) A vent 4 provided between the second hopper 3 and the die 2;

(5) At least two first kneading zones 5, 5', . . . provided between the first hopper 1 and the second hopper 3; and

(6) At least one second kneading zone 6 provided between the second hopper 3 and the vent 4;

(c) The resin temperature in L/D 3.5-7.5 upstream of the second hopper 3 is 290°-320° C.;

(d) The resin temperature in other zones is 260°-290° C.; and

(e) The resin temperature at the die exit is 260°-290° C.

When the L/D ratio of the double-screw extruder is less than 25, sufficient blending cannot be achieved. The preferred L/D ratio is 25-35.

The first hopper (the main hopper) 1, the second hopper 3, the vent 4 and the die 2 may have known structures.

The distance between the second hopper 3 and the die 2 is L/D 5-20. When it is less than L/D 5, sufficient blending cannot be achieved between the resin components and the glass fibers. On the other hand, when it exceeds L/D 20, the deterioration of the resin components and the breakage of the glass fibers are likely to take place. In this connection, the distance between the first hopper 1 and the second hopper 3 is preferably L/D 15-20.

The distance between the second hopper 3 and the vent 4 is preferably L/D 2.5-10. When it is less than L/D 2.5, sufficient venting effects cannot be obtained because the tying agents of the glass fibers are still in an unmolten state. On the other hand, when it exceeds 10, venting up may take place.

Both of the first kneading zones 5, 5' and the second kneading zone 6 are preferably L/D 1-4 and constituted by 4 or more kneading discs each having L/D of 1/4 or so. Incidentally, each kneading zone has preferably the structure as illustrated in FIG. 2.

Specifically speaking, a plurality of the kneading discs 12, 12' . . . arranged on the intermediate portions of the two screws 10, 11 form a kneading zone N, which is sandwiched by screw zones S, S'. In the kneading zone N, kneading discs 12, 12' . . . are arranged in pair, each fixed to each screw shaft. FIG. 3 shows a cross section of a pair of kneading discs 12, 12'. Each kneading disc 12, 12' has a peripheral surface in the form of a cam, each having projecting portions 13, 13' and circular portions 14, 14'. In each pair, the kneading discs 12, 12' are fixed to the screw shafts (not shown) by spline grooves 15, 15' such that each of the projecting portions 13, 13' and each of the circular portions 14, 14' are opposing to each other. Accordingly, in each pair, a gap between the kneading discs 12, 12' drastically changes by the rotation of the screw shafts. As shown in FIG. 2, since a plurality of the kneading discs 12, 12' . . . are arranged continuously, the resin components passing through each pair of the kneading discs (or mixtures of the resin components and the glass fibers) are subjected to much stronger blending action than by the screws. Incidentally, in FIG. 2, a transition zone (seal ring) T is provided downstream of the kneading discs 12, 12' in the kneading zone N, so that the blended product does not easily go out of the kneading zone.

In the above-described structure, it is necessary that there are at least one, preferably two or more, first kneading zone and at least one second kneading zone.

Without the first kneading zone 5, 5' . . . , or if it does not have sufficient length, the resin components would not be well blended, so that they are not sufficiently plasticized.

When the second kneading zone 6 has a length smaller than L/D 1 due to the insufficiency of kneading discs, the resins are too cooled by the addition of the glass fibers, so that the mixing of the glass fibers with the resins is hindered, and that surging tends to take place.

In general, a front end of the first kneading zone 5, 5' is located at L/D 5-20 downstream of the first hopper 1, and the total length of the first kneading zone is L/D 2-8 or so. A front end of the second kneading zone 6 is located at L/D 2-6 downstream of the second hopper 3, and the total length of the second kneading zone is L/D 1-4 or so.

When the resin temperature in a zone of L/D 3.5-7.5 upstream of the second hopper 3 does not reach the range of 290°-320° C., the glass fibers are prevented from being mixed with the resin components, and surging may take place. However, when the resin temperature is too high, the resins may be deteriorated, failing to provide the desired properties. In the other zones, the resin temperature is 260°-290° C. Incidentally, the resin temperature at the die exit is preferably 260°-290° C.

In the above double-screw extruder, the resin components are introduced into the double-screw extruder through the first hopper (the main hopper) 1, and the glass fibers are introduced into the double-screw extruder through the second hopper 3, and the two screws are rotated at 100-300 rpm to blend the resin components and the glass fibers. The compositions obtained by blending are extruded through the die exit 2 in the form of strand, and they are cut into pellets.

The fiber-reinforced polymer compositions of the present invention produced by the above double-screw extruder may easily be formed into desired shapes by a usual injection-molding method.

As described in detail above, although the polyamide resins and the polyolefins themselves do not have good compatibility, their compatibility is improved by the addition of the unsaturated carboxylic acid-modified polyolefins. The reason therefor seems to be that a reaction between the end amino groups of the polyamide resins and the carboxyl groups of the modified polyolefins takes place to form polyamide-modified polyolefin graft copolymers. Accordingly, a good compatibilizing effect can be obtained by adjusting the amount of the graft copolymers produced by selecting a molar ratio of the end amino groups to the carboxyl groups in the desired range of 10-1000. In this case, the fiber-reinforced polymer compositions have a morphology in which the polyamide resins form continuous phases, and the polyolefins form fine domains having an average size of 0.5-5 μm. The polyolefin domains are effective to provide proper compatibility to the polyamide resins and the polyolefins. Incidentally, when the polyolefin domain size is less than 0.5 μm, sufficient compatibility cannot be obtained. On the other hand, when it exceeds 5 μm, the fiber-reinforced polymer compositions show poor mechanical properties because cracks tend to appear on the domain surfaces by external stress.

When the glass fibers are surface-treated with the silane coupling agents and the tying agents made of polymers containing carboxyl groups or their anhydride groups, the adhesion of the glass fibers to the matrix resins is remarkably improved. This seems to be due to the fact that the carboxyl groups or their anhydride groups in the tying agents are reacted with he end amino groups of the polyamide resins.

The addition of the inorganic fillers serves to drastically improve the mechanical properties of the compositions, because the inorganic fillers act as rigid filling materials in the compositions, thereby improving the modulus of the entire compositions, and because they serve as nucleating agents for the polyamide resins, thereby increasing the crystallinity of the polyamide resins.

When the nucleating agents are added, the fiber-reinforced polymer compositions show drastically improved impact resistance and modulus. This seems to be due to fact that by the addition of the nucleating agents, spherulites of the polyamide resins and the polyolefins are made finer, thereby increasing the affinity between the crystal particles themselves and between the resin components and the glass fibers, and also increasing the crystallinity of the resins.

When nylon 66 and nylon 6 are used as polyamide resins in a particular proportion, the resulting fiber-reinforced polymer compositions have drastically improved impact resistance. This seems to be due to the fact that since nylon 66 and nylon 6 are partially dissolved in each other to prevent crystallization, the compatibility of nylon 66 and nylon 6 with the polyolefins is improved, thereby increasing the ductility of the compositions.

When the polyamide resins consist of nylon 46, and may contain nylon 66 and/or nylon 6, if necessary the resulting compositions show extremely improved heat resistance, mechanical properties, and creep resistance. This seems to be due to the fact that nylon 46 having high crystallinity, high thermal deformation temperature and excellent creep resistance is added to the polymer compositions.

Further, when the polyamide resins consist of nylon 12, nylon 612 or nylon 11, and if necessary, nylon 66 and/or nylon 6, the compositions show improved moldability, chemical resistance, antifreeze resistance and water absorption resistance. This seems to be due to the fact that nylon 12, nylon 612 and nylon 11 have relatively long methylene chains, showing polyolefinic properties.

According to the present invention, strong and stable blending between the resin components and the glass fibers can be achieved by using the double-screw extruder having the first kneading zone and the second kneading zone, thereby achieving the uniform dispersion of the polyamide resins and the polyolefins which do not have good compatibility. Thus, the resulting compositions show excellent mechanical strength and heat resistance.

The present invention will be described in further detail by the following Examples.

In each Example and Comparative Example, the properties of the fiber-reinforced polymer compositions were measured as follows:

(1) MFR

Measured at 275° C. under a load of 2160 g according to JIS K7210.

(2) Thermal deformation temperature

A test piece (cantilever) of 110 mm×4 mm×12.7 mm was bent under a constant load of 18.6 kg at a constant temperature elevating rate of 2° C./minute, and a temperature at which the test piece was bent by a predetermined amount (0.25 mm) was measured according to JIS K7207.

(3) Tensile strength

Measured at 23° C. and 140° C. respectively, according to JIS K 7113.

(4) Flexural Modulus

Measured at 23° C. and 140° C. respectively, according to JIS K 7203.

(5) Izod impact strength

Measured at 23° C. and -40° C. respectively, according to JIS K 7110.

(6) Antifreeze resistance

A test piece was immersed in a 50% aqueous solution of a commercially available long life automobile coolant at 140° C. for 200 hours, and the tensile strength of the test piece in a water-absorbed state was measured. The antifreeze resistance is expressed by a tensile strength retention ratio (%), assuming that the original tensile strength is 100.

(7) Geer oven life

After heating a test piece in a Geer oven at 150° C. for 3000 hours, a tensile strength retention ratio was measured.

Incidentally, in the tests (3)-(5), they were measured both under dry conditions and under water-absorbed conditions. The dry conditions mean that an injection-molded test piece was placed in a desiccator and kept at 23° C. for 75 hours, and the water-absorbed conditions mean that the injection-molded test piece was immersed in water at 100° C. for 24 hours.

EXAMPLES 1-5

Nylon, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 1, and introduced into a double-screw extruder of 45 mm in inner diameter through its main hopper. Further, chopped strands of glass fibers having an average diameter of 13 μm and an average length of 3 mm were introduced into the double-screw extruder at its intermediate position in proportions shown in Table 1 to produce composition pellets.

The composition pellets were dried in a drying furnace, and then formed into test pieces by injection molding to measure the properties shown in Table 1. The results are shown in Table 1.

                  TABLE 1                                                          ______________________________________                                         Example No.  1       2       3     4     5                                     ______________________________________                                         COMPOSITION                                                                    (wt. %).sup.(1)                                                                Nylon 66.sup.(2)                                                                            60      60      60    60    60                                    Polypropylene.sup.(3)                                                                       38.8    28      35    35    39                                    Modified Poly-                                                                 propylene.sup.(4)                                                              Grafted Acid Content                                                                        0.2     0.25    0.2   0.2   1.0                                   Content      1.2     12       5     5     1                                    Glass Fiber.sup.(5)                                                                         35      35      35    40    35                                    Molar Ratio of Amino                                                                        83      10      20    20    20                                    Group/Carboxyl                                                                 Group                                                                          Average Size of                                                                              4      0.7      2     2     2                                    Polypropylene                                                                  Domain (μm)                                                                 PROPERTIES                                                                     MFR (g/10 minutes)                                                                          20      8.5     14    14    14                                    Thermal Deformation                                                                         240     230     240   240   240                                   Temp. (°C.)                                                             Under Dry Conditions                                                           Tensile Strength                                                                            2300    2200    2300  2600  2300                                  (23° C.) (kg/cm.sup.2)                                                  (140° C.)                                                                            1100    1000    1100  1400  1100                                  Flexural Modulus                                                                            80000   77000   82000 89000 82000                                 (23° C.) (kg/cm.sup.2)                                                  (140° C.)                                                                            30000   29000   30000 35000 30000                                 Izod Impact Strength                                                                        16      15      16    17    16                                    (kg.cm/cm) (23° C.)                                                     (-40° C.)                                                                            12      12      12    13    12                                    Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength                                                                            1500    1500    1500  1800  1500                                  (23° C.) (kg/cm.sup.2)                                                  Flexural Modulus                                                                            60000   58000   61000 70000 61000                                 (23° C.) (kg/cm.sup.2)                                                  Izod Impact Strength                                                                        18      17      18    18    18                                    (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance                                                                       85      85      85    85    85                                    (%)                                                                            Geer Oven Life (%)                                                                          90      90      90    90    90                                    ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the content of      glass fibers is expressed by weight % based upon the total composition.        .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(4) Maleic anhydridemodified polypropylene.                               .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

COMPARATIVE EXAMPLES 1-3

Fiber-reinforced polymer compositions were produced in proportions shown in Table 2 under the same conditions as in the above Examples except for changing the amino group/carboxyl group molar ratios outside the range of 10-1000, and the same measurements were conducted. The results are shown in Table 2.

                  TABLE 2                                                          ______________________________________                                         Comparative Example No.                                                                             1       2       3                                         ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polypropylene.sup.(3)                                                                               39.95   25      35                                        Modified Polypropylene.sup.(4)                                                 Grafted Acid Content 0.2     0.2     1.0                                       Content              0.05    15       5                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         2000    6.4      4                                        Carboxyl Group                                                                 Average Size of      10      0.2     <0.1                                      Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)   35       5       3                                        Thermal Deformation Temp.                                                                           200     160     160                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    1500    1800    1800                                      (kg/cm.sup.2)                                                                  (140° C.)     750     500     500                                       Flexural Modulus (23° C.)                                                                    50000   82000   80000                                     (kg/cm.sup.2)                                                                  (140° C.)     13000   23000   20000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                           9       9       9                                        (-40° C.)      8       8       8                                        Under Water-Absorbed Conditions                                                Tensile Strength (23°  C.)                                                                   1000    1200    1200                                      (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                    35000   60000   59000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 11      11      11                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           80      80      80                                        Geer Oven Life (%)   90      90      90                                        ______________________________________                                          Note: .sup.(1) -.sup.(5) Same as in Table 1.                             

As is clear from the above results, the fiber-reinforced polymer compositions of the present invention, which not only contain the unsaturated carboxylic acid-modified polypropylene serving to increase the compatibility of the polyamide resin and the polypropylene, but also have molar ratios of amino groups/carboxyl groups set in the predetermined range as well as an average size of polypropylene domains within the range of 0.5-5 μm, show excellent mechanical strength, heat resistance, moldability, antifreeze resistance, etc.

EXAMPLES 6-8

Nylon 66, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 3, and introduced into a double-screw extruder shown in FIG. 1 through its main hopper.

The double-screw extruder used had the following structure:

    ______________________________________                                         Outer diameter of screw                                                                          45 mm                                                        L/D ratio         28                                                           Position of second hopper                                                                        At L/D 14 downstream of                                                        first hopper.                                                Position of vent  At L/D 5.5 upstream                                                            of die                                                       First kneading zone                                                            Number            2                                                            Position          At L/D 2 and L/D 4                                                             upstream of second hopper                                    Size of each      L/D = 1/4                                                    kneading disc                                                                  Number of kneading                                                                               6                                                            discs                                                                          Second kneading zone                                                           Number            1                                                            Position          At L/D 7 upstream of die                                     Size of each      L/D = 1/4                                                    kneading disc                                                                  Number of         4                                                            kneading discs                                                                 ______________________________________                                    

The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 3 into the double-screw extruder through its second hopper. The temperatures in various portions of the double-screw extruder were as follows:

    ______________________________________                                         Zone between L/D 3.5 and 7.5                                                                        290° C.                                            upstream of the second hopper                                                  Other zones          270° C.                                            ______________________________________                                    

With this double-screw extruder having screws rotating at 200 rpm, composition pellets were produced. The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 3.

                  TABLE 3                                                          ______________________________________                                         Example No.          6       7       8                                         ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polypropylene.sup.(3)                                                                               35      38.8    28                                        Modified Polypropylene.sup.(4)                                                 Grafted Acid Content 0.2     0.2     0.25                                      Content               5      1.2     12                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         20      83      10                                        Carboxyl Group                                                                 Average Size of       2       4      0.7                                       Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)   14      20      8.5                                       Thermal Deformation Temp.                                                                           240     240     230                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    2300    2300    2200                                      (kg/cm.sup.2)                                                                  (140° C.)     1100    1100    1000                                      Flexural Modulus (23° C.)                                                                    82000   80000   79000                                     (kg/cm.sup.2)                                                                  (140° C.)     30000   30000   29000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                          16      16      15                                        (-40° C.)     12      12      12                                        Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                    1500    1500    1500                                      (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                    61000   60000   58000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 18      18      17                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           85      85      85                                        Geer Oven Life (%)   90      90      90                                        ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the content of      glass fibers is expressed by weight % based upon the total composition.        .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(4) Maleic anhydridemodified homopolypropylene                            .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

EXAMPLES 9-11

Fiber-reinforced polymer compositions were produced in proportions shown in Table 4 under the same conditions as in Examples 6-8 except for changing polypropylene to polyethylene (J-6311, manufactured by Tonen Sekiyu Kagaku K.K.), and the same tests were conducted. The results are shown in Table 4.

                  TABLE 4                                                          ______________________________________                                         Example No.          9       10      11                                        ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polyethylene.sup.(3) 35      38.8    28                                        Modified Polyethylene.sup.(4)                                                  Grafted Acid Content 0.2     0.2     0.25                                      Content               5      1.2     12                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         20      83      10                                        Carboxyl Group                                                                 Average Size of       3      4.5      1                                        Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes)   16      21      8.5                                       Thermal Deformation Temp.                                                                           240     240     230                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    1900    1900    1900                                      (kg/cm.sup.2)                                                                  (140° C.)     900     900     900                                       Flexural Modulus (23° C.)                                                                    70000   70000   70000                                     (kg/cm.sup.2)                                                                  (140° C.)     25000   25000   25000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                          20      20      19                                        (-40° C.)     17      17      16                                        Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                    1500    1500    1500                                      (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                    50000   50000   50000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 23      23      21                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           87      87      87                                        Geer Oven Life (%)   92      92      92                                        ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the content of          glass fibers is expressed by weight % based upon the total composition.        .sup.(2), .sup.(5) Same as in Table 3.                                         .sup.(3) J6311 manufactured by Tonen Sekiyu Kagaku K.K.                        .sup.(4) Maleic anhydridemodified highdensity polyethylene.              

COMPARATIVE EXAMPLE 4

A fiber-reinforced polymer composition was produced in a proportion shown in Table 5 under the same conditions as in Example 6 except for adding no modified polypropylene, and the same tests were conducted. The results are shown in Table 5.

COMPARATIVE EXAMPLE 5

A fiber-reinforced polymer composition was produced in a proportion shown in Table 5 under the same conditions as in Example 6 except for using modified polypropylene (graft content: 1.0 weight %) in such an amount as to form polypropylene domains having an average size of less than 0.1 μm, and the same tests were conducted. The results are shown in Table 5.

COMPARATIVE EXAMPLE 6

A fiber-reinforced polymer composition was produced by lightly blending the components in a proportion shown in Table 5 by a Brabender Plastograph, and the same tests were conducted. The results are shown in Table 5.

                  TABLE 5                                                          ______________________________________                                         Comparative Example No.                                                                             4       5       6                                         ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polypropylene.sup.(3)                                                                               40      35      35                                        Modified Polypropylene.sup.(4)                                                 Grafted Acid Content --      1.0     0.2                                       Content               0       5       5                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         --      3.8     20                                        Carboxyl Group                                                                 Average Size of      15      <0.1    10                                        Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)   35       3      25                                        Thermal Deformation Temp.                                                                           220     160     220                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    1800    1800    1800                                      (kg/cm.sup.2)                                                                  (140° C.)     800     500     800                                       Flexural Modulus (23° C.)                                                                    55000   80000   55000                                     (kg/cm.sup.2)                                                                  (140° C.)     15000   20000   15000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                           9       9       9                                        (-40° C.)      8       8       8                                        Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                    1200    1200    1200                                      (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                    35000   59000   35000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 10      11      10                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           80      80      80                                        Geer Oven Life (%)   90      90      90                                        ______________________________________                                          Note: .sup.(1) -.sup.(5) Same as in Table 3.                             

COMPARATIVE EXAMPLES 7-9

Fiber-reinforced polymer compositions were produced in proportions shown in Table 6 under the same conditions as in Comparative Examples 4-6 except for changing polypropylene to polyethylene, and the same tests were conducted. The results are shown in Table 6.

                  TABLE 6                                                          ______________________________________                                         Comparative Example No.                                                                             7       8       9                                         ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polyethylene.sup.(3) 40      35      35                                        Modified Polyethylene.sup.(4)                                                  Grafted Acid Content --      1.0     0.2                                       Content              --       5       5                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         --      3.8     20                                        Carboxyl Group                                                                 Average Size of      18      <0.1    14                                        Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes)   38       5      30                                        Thermal Deformation Temp.                                                                           210     140     210                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    1500    1600    1500                                      (kg/cm.sup.2)                                                                  (140° C.)     600     400     600                                       Flexural Modulus (23° C.)                                                                    45000   60000   45000                                     (kg/cm.sup.2)                                                                  (140° C.)     10000   15000   10000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                          12      12      12                                        (-40° C.)     10      10      10                                        Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                    1000    1100    1000                                      (kg/cm.sup.2 )                                                                 Flexural Modulus (23° C.)                                                                    30000   45000   30000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 13      13      13                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           87      87      87                                        Geer Oven Life (%)   92      92      92                                        ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the content of          glass fibers is expressed by weight % based upon the total composition.        .sup.(2) -.sup.(5) Same as in Table 4.                                   

As is clear from the results in Tables 3-6, since the fiber-reinforced polymer compositions of the present invention contain polypropylene or polyethylene domains having an average size of 0.5-5 μm and uniformly dispersed in nylon phases, they show excellent mechanical strength, impact resistance and thermal resistance. On the other hand, the fiber-reinforced polymer compositions in the Comparative Examples containing polypropylene or polyethylene domains having an average size outside the above range have poor thermal deformation resistance and mechanical properties.

EXAMPLES 12-16

Nylon, polyethylene and modified polyethylene were dry-blended in a high-speed mixer in proportions shown in Table 7, and introduced into a double-screw extruder of 45 mm in diameter through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 7 into the double-screw extruder through its second hopper, and they were blended at a temperature of 280° C. to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 7.

                  TABLE 7                                                          ______________________________________                                         Example No.  12      13      14    15    16                                    ______________________________________                                         COMPOSITION                                                                    (wt. %).sup.(1)                                                                Nylon 66.sup.(2)                                                                            60      60      60    60    60                                    Polyethylene.sup.(3)                                                                        38.8    28      35    35    39                                    Modified Poly-                                                                 ethylene.sup.(4)                                                               Grafted Acid Content                                                                        0.2     0.25    0.2   0.2   1.0                                   Content      1.2     12       5     5     1                                    Glass Fiber.sup.(5)                                                                         35      35      35    40    35                                    Molar Ratio of Amino                                                                        83      10      20    20    20                                    Group/Carboxyl                                                                 Group                                                                          Average Size of                                                                              4      0.7      3     3     3                                    Polyethylene                                                                   Domain (μm)                                                                 PROPERTIES                                                                     MFR (g/10 minutes)                                                                          28      15      20    20    20                                    Thermal Deformation                                                                         240     230     240   240   240                                   Temp. (°C.)                                                             Under Dry Conditions                                                           Tensile Strength                                                                            1700    1600    1700  1900  1700                                  (23° C.) (kg/cm.sup.2)                                                  (140° C.)                                                                            900     800     900   1100  900                                   Flexural Modulus                                                                            70000   69000   72000 79000 72000                                 (23° C.) (kg/cm.sup.2)                                                  (140° C.)                                                                            25000   24000   25000 30000 25000                                 Izod Imapct Strength                                                                        19      18      19    19    18                                    (kg.cm/cm) (23° C.)                                                     (-40° C.)                                                                            18      18      18    19    18                                    Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength                                                                            1400    1400    1400  1600  1400                                  (23° C.) (kg/cm.sup.2)                                                  Flexural Modulus                                                                            53000   51000   54000 64000 54000                                 (23° C.) (kg/cm.sup.2)                                                  Izod Impact Strength                                                                        20      19      20    20    20                                    (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance                                                                       90      90      90    90    90                                    (%)                                                                            Geer Oven Life (%)                                                                          95      95      95    95    95                                    ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the content of          glass fibers is expressed by weight % based upon the total composition.        .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) Highdensity polyethylene J6311 manufactured by Tonen Sekiyu           Kagaku K.K.                                                                    .sup.(4) Maleic anhydridemodified polyethylene.                                .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

COMPARATIVE EXAMPLES 10-12

Fiber-reinforced polymer compositions were produced in proportions shown in Table 8 under the same conditions as in Examples 12-16 except for changing the amino group/carboxyl group molar ratios outside the range of 10-1000, and the same measurements were conducted. The results are shown in Table 8.

                  TABLE 8                                                          ______________________________________                                         Comparative Example No.                                                                             10      11      12                                        ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)     60      60      60                                        Polyethylene.sup.(3) 39.95   25      35                                        Modified Polyethylene.sup.(4)                                                  Grafted Acid Content 0.2     0.2     1.0                                       Content              0.05    15       5                                        Glass Fiber.sup.(5)  35      35      35                                        Molar Ratio of Amino Group/                                                                         2000    6.4      4                                        Carboxyl Group                                                                 Average Size of      10      0.3     <0.1                                      Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes)   40      10       7                                        Thermal Deformation Temp.                                                                           200     150     150                                       (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (23° C.)                                                                    1200    1400    1400                                      (kg/cm.sup.2)                                                                  (140° C.)     400     350     350                                       Flexural Modulus (23° C.)                                                                    40000   72000   70000                                     (kg/cm.sup.2)                                                                  (140° C.)     8000    18000   15000                                     Izod Impact Strength                                                           (kg.cm/cm) (23° C.)                                                                          10      10      10                                        (-40° C.)      9       9       9                                        Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                    9000    1100    1100                                      (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                    27000   53000   52000                                     (kg/cm.sup.2)                                                                  Izod Impact Strength 13      13      13                                        (kg.cm/cm) (23° C.)                                                     Antifreeze Resistance (%)                                                                           85      85      85                                        Geer Oven Life (%)   90      90      90                                        ______________________________________                                          Note:.sup.(1) -.sup.(5) Same as in Table 7.                              

As is clear from Tables 7 and 8, the fiber-reinforced polymer compositions of the present invention not only containing the unsaturated carboxylic acid-modified polyethylene serving to increase the compatibility of the polyamide resin and the polyethylene but also having molar ratios of amino groups/carboxyl groups set in the predetermined range are excellent in mechanical strength and heat resistance, and particularly in heat deterioration resistance, moldability, antifreeze resistance, etc.

EXAMPLES 17

Nylon 66, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 9, and introduced into a double-screw extruder shown in FIG. 1 through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 9 into the double-screw extruder through its second hopper.

The double-screw extruder used had the following structure:

    ______________________________________                                         Outer diameter of screw                                                                          45 mm                                                        L/D ratio         28                                                           Position of second hopper                                                                        At L/D 10 downstream of                                                        first hopper.                                                Position of vent  At L/D 5.5 upstream                                                            of die                                                       First kneading zone                                                            Number            2                                                            Position          In L/D 2-3.5 and L/D 5-6.5                                                     upstream of second hopper                                    Size of each      L/D = 1/4                                                    kneading disc                                                                  Number of kneading                                                                               6                                                            discs                                                                          Second kneading zone                                                           Number            1                                                            Position          At L/D 7 upstream of die                                     Size of each      L/D = 1/4                                                    kneading disc                                                                  Number of         4                                                            kneading discs                                                                 The temperatures in various portions of the                                    double-screw extruder were as follows:                                         Zone between L/D 3.5 and 7.5                                                                     300° C.                                               upsteam of the second hopper                                                   Other zones (L/D 7.5-25)                                                                         280° C.                                               ______________________________________                                    

With this double-screw extruder having screws rotating at 200 rpm, composition pellets were produced. The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 9.

EXAMPLE 18

A fiber-reinforced polymer composition was produced in a proportion shown in Table 9 under the same conditions as in Example 17 except for changing the number of the first kneading zone to 1 and the number of the kneading discs to 8, and the same tests were conducted. The results are shown in Table 9.

COMPARATIVE EXAMPLE 13

A fiber-reinforced polymer composition was produced in a proportion shown in Table 9 under the same conditions as in Example 17 except for changing the number of the first kneading zone to 1 and using 3 kneading discs in the first kneading zone, and the same tests were conducted. The results are shown in Table 9.

COMPARATIVE EXAMPLE 14

A fiber-reinforced polymer composition was produced under the same conditions as in Example 17 except for using a double-crew extruder not having first and second kneading zones. However, since the resin components were insufficiently plasticized, they could not be blended. Thus, the property tests were not conducted.

COMPARATIVE EXAMPLE 15

A fiber-reinforced polymer composition was produced under the same conditions as in Example 17 except for changing the number of the first kneading zone to 1 and adjusting the resin temperature at 260° C. in a zone of L/D 3.5 to L/D 7.5. However, as in Comparative Example 15, the resin components were insufficiently plasticized, so that they could not be blended. Thus, the property tests were not conducted.

                                      TABLE 9                                      __________________________________________________________________________                      Example     Comparative Example                                                17    18    13    14  15                                      __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2) 60    60    60     60  60                                     Polypropylene.sup.(3)                                                                           35    35    35     35  35                                     Modified Polypropylene.sup.(4)                                                 Grafted Acid Content                                                                            0.2   0.2   0.2      0.2                                                                                0.2                                  Content          5     5     5      5   5                                      Glass Fiber.sup.(5)                                                                             35    35    35     35  35                                     Average Size of  2     3     10    --  --                                      Polypropylene Domain (μm)                                                   PRODUCTION CONDITIONS                                                          First Kneading Zone                                                            Number           2     1     1      0   1                                      Number of Kneading Discs                                                                        6     8     3     --   6                                      Second Kneading Zone                                                           Number           1     1     1      0   1                                      Number of Kneading Discs                                                                        4     4     4     --   4                                      Resin Temp. in Extruder (°C.)                                           L/D 3.5-7.5      300   300   300   300 260                                     L/D 7.5-25       280   280   280   280 280                                     PROPERTIES                                                                     MFR (g/10 minutes)                                                                              14    16    20    --  --                                      Thermal Deformation Temp.                                                                       240   240   235   --  --                                      (°C.)                                                                   Tensile Strength (kg/cm.sup.2)                                                  (23° C.) 2300  2200  1800  --  --                                      (140° C.) 1100  1100  800   --  --                                      Flexural Modulus (kg/cm.sup.2)                                                  (23° C.) 82000 82000 55000 --  --                                      (140° C.) 30000 30000 15000 --  --                                      Izod Impact Strength (kg · cm/cm)                                      (23° C.) 16    15    10    --  --                                      (-40° C.) 12    11    8     --  --                                      Antifreeze Resistance (%)                                                                       85    85    --    --  --                                      __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the content of      glass fibers is expressed by weight % based upon the total composition.        .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup. (4) Maleic anhydridemodified homopolypropylene (graft content: 0.2       weight %).                                                                     .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

As is clear from the results in Table 9, the fiber-reinforced polymer compositions produced by the method of the present invention show excellent mechanical strength, heat resistance and antifreeze resistance, while those produced by the method of Comparative Examples are poor in the above properties. Further, under certain conditions, blending cannot be conducted due to the failure of plasticizing the resin components Comparative Examples 15 and 16).

EXAMPLES 19-23, COMPARATIVE EXAMPLES 16-18

Nylon, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 11, and introduced into a double-screw extruder of 45 mm in diameter through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 11 into the double-screw extruder through its second hopper and blended with resin components at a temperature of 280° C. to provide composition pellets. Incidentally, the glass fibers used were surface-treated with treatment agents comprising silane coupling agents and carboxyl group (or anhydride)-containing polymer tying agents in proportions as shown in Table 10. The surface treatment of the glass fibers was conducted by immersing them in aqueous emulsions of the treatment agents and drying them at 120° C. for 5 minutes. The amount of the treatment agent applied in each Example is also shown in Table 10.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 11.

                  TABLE 10                                                         ______________________________________                                                Surface Treatment Aqent for Glass Fiber                                        Silane                                                                         Coup- Polymer               Amount.sup.(2)                                     ling  for Tying     Weight  (Parts by                                          Agent Agent         Ratio.sup.(1)                                                                          Weight)                                     ______________________________________                                         Example No.                                                                    19       Amino   Maleic anhydride-                                                                            1:10  3                                                  silane  styrene copolymer                                             20       Amino   Acrylic acid- 1:10  3                                                  silane  styrene copolymer                                             21       Epoxy   Maleic anhydride-                                                                            1:10  3                                                  silane  styrene copolymer                                             22       Amino   Maleic anhydride-                                                                            1:10  3                                                  silane  styrene copolymer                                             23       Amino   Maleic anhydride-                                                                            1:10  3                                                  silane  styrene copolymer                                             Comparative                                                                    Example No.                                                                    16       Amino   Epoxy resin   1:10  3                                                  silane                                                                17       Amino   Polyurethane  1:10  3                                                  silane                                                                18       --        --          --    --                                        ______________________________________                                          Note:                                                                          .sup.(1) Ratio of silane coupling agent:Polymer tying agent.                   .sup.(2) Amount per 100 parts by weight of glass fibers.                 

                                      TABLE 11                                     __________________________________________________________________________                    Example No.                   Comparative Example No.                          19    20    21    22    23    16    17    18                    __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                              60    60    60    60    60    60    60    60                    Polypropylene.sup.(3)                                                                         35    35    35    38.8  28    35    35    35                    Modified Polypropylene.sup.(4)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.25  0.2   0.2   0.2                   Content        5     5     5     1.2   12    5     5     5                     Glass Fiber.sup.(5)                                                                           35    35    35    35    35    35    35    35                    Molar Ratio of Amino Group/                                                                   20    20    20    80    10    20    20    20                    Carboxyl Group                                                                 Average Size of                                                                               2     2     2     4     0.7   2     2     2                     Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)                                                                            14    14    14    20    8     18    18    18                    Thermal Deformation Temp.                                                                     240   240   240   240   230   200   200   190                   (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)                                                                              2300  2200  2200  2300  2200  2000  2000  1700                  (140° C.)                                                                              1100  1000  1000  1100  1000  600   600   450                   Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)                                                                              87000 82000 84000 87000 82000 65000 65000 55000                 (140° C.)                                                                              30000 30000 30000 30000 30000 12000 12000 9000                  Izod Impact Strength (Kg · cm/cm)                                      (23° C.)                                                                              16    15    15    16    15    12    12    10                    (-40° C.)                                                                              12    11    11    12    12    8     8     6                     Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength (23° C.)                                                              1500  1500  1500  1500  1200  1200  1200  1000                  (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                              61000 60000 60000 61000 60000 40000 41000 35000                 (kg/cm.sup.2)                                                                  Izod Impact Strength (23° C.)                                                          18    17    17    18    17    15    15    12                    (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                     85    85    85    85    85    50    50    40                    __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the content of      glass fibers is expressed by weight % based upon the total composition.        .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(4) Maleic anhydridemodified polypropylene.                               .sup.(5) Glass fibers treated with the treatment agents shown in Table 10                                                                               

EXAMPLES 24 AND 25

Fiber-reinforced polymer compositions were produced in proportions shown in Table 12 under the same conditions as in Examples 19 and 20 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above polyethylene modified with carboxylic acids shown in Table 12 as the modified polyethylene, and the same measurements as in Examples 19 and 20 were conducted. The results are shown in Table 12.

                  TABLE 12                                                         ______________________________________                                                          Example No.                                                                    24      25                                                    ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)   60        60                                                Polyethylene.sup.(3)                                                                              35        35                                                Modified Polyethylene.sup.(4)                                                  Grafted Acid Content                                                                              0.2       0.2                                               Content            5         5                                                 Glass Fiber.sup.(5)                                                                               35        35                                                Molar Ratio of Amino Group/                                                                       20        20                                                Carboxyl Group                                                                 Average Size of    3         3                                                 Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes) 16        16                                                Thermal Deformation Temp.                                                                         240       240                                               (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)   1900      1800                                              (140° C.)   900       850                                               Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)   72000     70000                                             (140° C.)   25000     24000                                             Izod Impact Strength (kg · cm/cm)                                      (23° C.)   21        20                                                (-40° C.)   18        17                                                Under Water-Absorbed Conditions                                                Tensile Strength (23° C.)                                                                  1600      1600                                              (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                                  50000     50000                                             (kg/cm.sup.2)                                                                  Izod Impact Strength (23° C.)                                                              24        24                                                (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                         88        88                                                ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the content of          glass fibers is expressed by weight % based upon the total composition.        .sup.(2), (5) Same as in Table 11.                                             .sup.(3) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.).                                                                  .sup.(4) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results in Tables 11 and 12, since the fiber-reinforced polymer compositions of the present invention contain not only the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also the glass fibers treated with the silane coupling agents and the tying agents consisting of polymers having carboxyl groups or their anhydrides, they show excellent mechanical strength, heat resistance, moldability, antifreeze resistance, etc.

EXAMPLES 26-30, COMPARATIVE EXAMPLES 19-21

Nylon, polypropylene, modified polypropylene and inorganic fillers were dry-blended in a high-speed mixer in proportions shown in Table 13, and introduced into a double-screw extruder of 45 mm in inner diameter through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 13 into the double-screw extruder through its second hopper. They were blended at 280° C. to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 13.

                                      TABLE 13                                     __________________________________________________________________________                    Example No.                   Comparative Example No.                          26    27    28    29    30    19    20    21                    __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                              60    60    60    60    60    60    60    60                    Polypropylene.sup.(3)                                                                         35    35    35    35    35    35    35    35                    Modified Polypropylene.sup.(4)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.2   0.2   0.2   0.1                   Content        5     5     5     5     5     5     5     5                     Glass Fiber.sup.(5)                                                                           35    35    35    35    35    35    35    35                    Molar Ratio of Amino Group/                                                                   20    20    20    20    20    20    20    20                    Carboxyl Group                                                                 Average Size of                                                                               2     2     2     2     2     2     2     2                     Polypropylene Domain (μm)                                                   Inorganic Filler                                                               Talc.sup.(6)   5     0     0     3     2     15    0     0                     Mica.sup.(7)   0     5     0     0     2     0     15    0                     Potassium Titanate.sup.(8)                                                                    0     0     5     3     2     0     0     15                    PROPERTIES                                                                     MFR (g/10 minutes)                                                                            10    9     10    10    11    8     7     8                     Thermal Deformation Temp.                                                                     245   245   240   245   245   240   240   240                   (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)                                                                              2800  2900  2800  2900  2900  2700  2800  2700                  (140° C.)                                                                              1500  1800  1400  1700  1800  1400  1500  1400                  Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)                                                                              90000 95000 90000 94000 95000 70000 90000 90000                 (140° C.)                                                                              40000 43000 40000 42000 44000 40000 40000 40000                 Izod Impact Strength                                                           (kg · cm/cm)                                                           (23° C.)                                                                              12    12    12    12    12    5     5     5                     (-40° C.)                                                                              8     8     8     8     8     4     4     4                     Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength (23° C.)                                                              1700  1800  1700  1800  1800  1600  1700  1600                  (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                              75000 78000 75000 78000 78000 50000 75000 75000                 (kg/cm.sup.2)                                                                  Izod Impact Strength (23° C.)                                                          14    14    14    14    14    7     7     7                     (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                     85    85    85    85    85    85    85    85                    __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the contents o      glass fibers and inorganic fillers are expressed by weight % based upon        the total composition.                                                         .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(4) Maleic anhydridemodified polypropylene.                               .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                        .sup.(6) 5000 PJ, size: 1-2 μm, manufactured by Matsumura Sangyo K.K.       .sup.(7) Suzulight Mica 200 HK, 200 mesh passed, manufactured by Kuraray       Co., Ltd.                                                                      .sup.(8) Tismo D, diameter: 0.2 0.5 m, length: 10-20 μm, manufactured       by Ohtsuka Kagaku K.K.                                                   

EXAMPLES 31-33

Fiber-reinforced polymer compositions were produced in proportions shown in Table 14 under the same conditions as in Examples 26-28 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above polyethylene modified with carboxylic acids shown in Table 14 as the modified polyethylene, and the same measurements as in Examples 26-28 were conducted. The results are shown in Table 14.

                                      TABLE 14                                     __________________________________________________________________________                     Example No.                                                                    31     32     33                                               __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                               60     60     60                                               Polyethylene.sup.(3)                                                                           35     35     35                                               Modified Polyethylene.sup.(4)                                                  Grafted Acid Content                                                                           0.2    0.2    0.2                                              Content         5      5      5                                                Glass Fiber.sup.(5)                                                                            35     35     35                                               Molar Ratio of Amino Group/                                                                    20     20     20                                               Carboxyl Group                                                                 Average Size of 3      3      3                                                Polyethylene Domain (μm)                                                    Inorganic Filler                                                               Talc.sup.(6)    5      0      0                                                Mica.sup.(7)    0      5      0                                                Potassium Titanate.sup.(8)                                                                     0      0      5                                                PROPERTIES                                                                     MFR (g/10 minutes)                                                                             15     13     15                                               Thermal Deformation Temp.                                                                      240    240    240                                              (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)                                                                               2000   2000   2000                                             (140° C.)                                                                               1200   1200   1200                                             Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)                                                                               82000  82000  81000                                            (140° C.)                                                                               35000  35000  35000                                            Izod Impact Strength                                                           (kg · cm/cm)                                                           (23° C.)                                                                               15     15     15                                               (-40° C.)                                                                               14     14     14                                               Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength (23° C.)                                                               1600   1600   1600                                             (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                               64000  64000  63000                                            (kg/cm.sup.2)                                                                  Izod Impact Strength (23° C.)                                                           17     17     17                                               (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                      90     90     90                                               __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the contents of         glass fibers and inorganic fillers are expressed by weight % based upon        the total composition.                                                         .sup.(2), (5)-(8) Same as in Table 13.                                         .sup.(3) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.)                                                                   .sup.(4) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results in Tables 13 and 14, the fiber-reinforced polymer compositions of the present invention contain not only the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also the above inorganic fillers, they show excellent mechanical properties such as tensile strength, flexural modulus and impact strength.

EXAMPLES 34-40, COMPARATIVE EXAMPLE 22

Nylon, polypropylene, modified polypropylene and nucleating agents were dry-blended in a high-speed mixer in proportions shown in Table 15, and introduced into a double-screw extruder of 45 mm in inner diameter shown in FIG. 1 through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 15 into the double-screw extruder through its second hopper. They were blended at 280° C. to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 15.

                                      TABLE 15                                     __________________________________________________________________________                                                              Compara-                                                                       tive                                 Example No.                               Example                              34    35    36    37    38    39    40    22                    __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                              60    60    60    60    60    60    60    60                    Polypropylene.sup.(3)                                                                         35    35    35    35    35    35    35    35                    Modified Polypropylene.sup.(4)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.2   0.2   0.2   0.2                   Content        5     5     5     5     5     5     5     5                     Glass Fiber.sup.(5)                                                                           35    35    35    35    35    35    35    35                    Molar Ratio of Amino Group/                                                                   20    20    20    20    20    20    20    20                    Carboxyl Group                                                                 Average Size of                                                                               2     2     2     2     2     2     2     2                     Polypropylene Domain (μm)                                                   Nucleating A.sup.(6)                                                                          0     0     0     0.5   0     0     0     0                     Agent B.sup.(7)                                                                               0.05  0.5   1.0   0     0     0.5   0.01  5                     C.sup.(8)      0     0     0     0     0.5   0.5   0     0                     PROPERTIES                                                                     MFR (g/10 minutes)                                                                            14    14    14    14    14    14    14    14                    Thermal Deformation Temp.                                                                     240   240   240   240   240   240   240   240                   (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)                                                                              2300  2300  2300  2300  2300  2300  2300  2300                  (140° C.)                                                                              1100  1100  1100  1100  1100  1100  1100  1100                  Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)                                                                              90000 93000 93000 90000 90000 94000 82000 90000                 (140° C.)                                                                              40000 42000 42000 40000 40000 43000 30000 40000                 Izod Impact Strength                                                           (kg · cm/cm)                                                          (23° C.)                                                                               20    23    24    20    20    24    16    23                     (-40° C.)                                                                             15    16    17    15    15    18    12    16                    Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength (23° C.)                                                              1500  1500  1500  1500  1500  1500  1500  1500                  (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                              70000 72000 72000 70000 70000 73000 61000 70000                 (kg/cm.sup.2)                                                                  Izod Impact Strength (23° C.)                                                          23    26    27    23    23    26    18    25                    (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                     88    88    89    87    88    88    85    88                    __________________________________________________________________________      Note                                                                           .sup.(1) The contents of nylon, polypropylene and modified polypropylene       are expressed by weight % based upon resin components, and the contents o      glass fibers and nucleating agents are expressed by weight % based upon        the total composition.                                                         .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(4) Maleic anhydridemodified polypropylene.                               .sup.(5) MA03FT2 manufactured by Asahi Fiber Glass K.K.                        .sup.(6) Sodium benzoate.                                                      .sup.(7) Aluminum Ptert-butyl monohydroxybenzoate.                             .sup.(8) Dibenzylidene sorbitol.                                         

EXAMPLES 41-43

Fiber-reinforced polymer compositions were produced in proportions shown in Table 16 under the same conditions as in Examples 34-36 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above high-density polyethylene modified with carboxylic acids shown in Table 16 as the modified polyethylene, and the same measurements as in Examples 34-36 were conducted. The results are shown in Table 16.

                                      TABLE 16                                     __________________________________________________________________________                     Example No.                                                                    41     42     43                                               __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                               60     60     60                                               Polyethylene.sup.(3)                                                                           35     35     35                                               Modified Polyethylene.sup.(4)                                                  Grafted Acid Content                                                                           0.2    0.2    0.2                                              Content         5      5      5                                                Glass Fiber.sup.(5)                                                                            35     35     35                                               Molar Ratio of Amino Group/                                                                    20     20     20                                               Carboxyl Group                                                                 Average Size of 3      3      3                                                Polyethylene Domain (μm)                                                    Nucleating A.sup.(6)                                                                           0      0      0                                                Agent B.sup.(7) 0.05   0.5    1.0                                              C.sup.(8)       0      0      0                                                PROPERTIES                                                                     MFR (g/10 minutes)                                                                             16     16     16                                               Thermal Deformation Temp.                                                                      240    240    240                                              (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength (kg/cm.sup.2)                                                  (23° C.)                                                                               1900   1900   1900                                             (140° C.)                                                                               900    900    900                                              Flexural Modulus (kg/cm.sup.2)                                                  (23° C.)                                                                               80000  82000  83000                                            (140° C.)                                                                               35000  36000  36000                                            Izod Impact Strength                                                           (kg · cm/cm)                                                           (23° C.)                                                                               25     26     26                                               (-40° C.)                                                                               20     20     21                                               Under Water-Absorbed                                                           Conditions                                                                     Tensile Strength (23° C.)                                                               1500   1500   1500                                             (kg/cm.sup.2)                                                                  Flexural Modulus (23° C.)                                                               60000  60000  61000                                            (kg/cm.sup.2)                                                                  Izod Ipact Strength (23° C.)                                                            28     28     29                                               (kg · cm/cm)                                                          Antifreeze Resistance (%)                                                                      90     90     90                                               __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon, polyethylene and modified polyethylene ar      expressed by weight % based upon resin components, and the contents of         glass fibers and nucleating agents are expressed by weight % based upon        the total composition.                                                         .sup.(2), (5)-(8) Same as in Table 15.                                         .sup.(3) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.).                                                                  .sup.(4) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results, since the fiber-reinforced polymer compositions of the present invention contain not only the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also the above nucleating agents, they show excellent mechanical strength, heat resistance, moldability, antifreeze resistance, etc., and their impact resistance and modulus are remarkably improved.

EXAMPLES 44-49

Nylon 66, nylon 6, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 17, and introduced into a double-screw extruder of 45 mm in inner diameter shown in FIG. 1 through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 17 into the double-screw extruder through its second hopper. They were blended at 280° C. to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 17.

                                      TABLE 17                                     __________________________________________________________________________                    Example No.                                                                    44    45    46    47    48    49                                __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)                                                                              50    40    30    40    40    10                                Nylon 6.sup.(3)                                                                               10    20    30    20    20    50                                Polypropylene.sup.(4)                                                                         35    35    35    38.8  28    35                                Modified Polypropylene.sup.(5)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.25  0.2                               Content        5     5     5     1.2   12    5                                 Glass Fiber.sup.(6)                                                                           35    35    35    35    35    35                                Molar Ratio of Amino Group/                                                                   20    21    21    83    10    22                                Carboxyl Group                                                                 Average Size of                                                                               2     2     2     4     0.8   2                                 Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)                                                                            8.5   8.0   8.8   15    0.5   8.0                               Thermal Deformation Temp.                                                                     230   220   210   220   210   190                               (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                        (23° C.)                                                                      1600  1500  1500  1500  1400  1300                              (kg/cm.sup.2)                                                                           (140° C.)                                                                     700   600   600   600   550   500                               Flexural Modulus                                                                        (23° C.)                                                                      70000 70000 67000 70000 68000 50000                             (kg/cm.sup.2)                                                                           (140° C.)                                                                     25000 24000 21000 24000 22000 10000                             Izod Impact Strength                                                           (kg · cm/cm)                                                                   (23° C.)                                                                      20    25    27    25    24    10                                         (-40° C.)                                                                     17    18    20    18    17    8                                 Under Water-Absorbed Conditions                                                Tensile Strength                                                                        (23° C.)                                                                      1000  1000  1000  1000  950   700                               (kg/cm.sup.2)                                                                  Flexural Modulus                                                                        (23° C.)                                                                      50000 50000 48000 50000 49000 35000                             (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg · cm/cm)                                                                   (23° C.)                                                                      23    28    29    28    27    12                                Antifreeze Resistance (%)                                                                     85    80    80    80    80    60                                __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon 66, nylon 6, polypropylene and modified         polypropylene are expressed by weight % based upon resin components, and       the content of glass fibers is expressed by weight % based upon the total      composition.                                                                   .sup.(2) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to a KorshakZamyationa method (back titration method)       (Chem. Abs. 40, 4665, '46, ibid 42, 6152, '48).                                .sup.(3) Amiran CM1017 manufactured by Toray Industries, Inc. and              containing end amino groups in an amount of 0.040 milliequivalent/g            measured according to the same KorshakZamyationa method as in (2).             .sup.(4) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(5) Maleic anhydridemodified polypropylene.                               .sup.(6) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

EXAMPLES 50 AND 51

Fiber-reinforced polymer compositions were produced in proportions shown in Table 18 under the same conditions as in Examples 44 and 45 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above high-density polyethylene modified with carboxylic acids shown in Table 18 as the modified polyethylene, and the same measurements as in Examples 44 and 45 were conducted. The results are shown in Table 18.

                  TABLE 18                                                         ______________________________________                                                          Example No.                                                                    50      51                                                    ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 66.sup.(2)   50        40                                                Nylon 6.sup.(3)    10        20                                                Polyethylene.sup.(4)                                                                              35        35                                                Modified Polyethylene.sup.(5)                                                  Grafted Acid Content                                                                              0.2       0.2                                               Content            5         5                                                 Glass Fiber.sup.(6)                                                                               35        35                                                Molar Ratio of Amino Group/                                                                       20        20                                                Carboxyl Group                                                                 Average Size of    3         3                                                 Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes) 12        10                                                Thermal Deformation Temp.                                                                         230       220                                               (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                          (23° C.)                                                                            1300      1200                                          (kg/cm.sup.2)                                                                             (140° C.)                                                                           500       450                                           Flexural Modulus                                                                          (23° C.)                                                                            68000     66000                                         (kg/cm.sup.2)                                                                             (140° C.)                                                                           20000     19000                                         Izod Imact Strength                                                            (kg · cm/cm)                                                                     (23° C.)                                                                            25        28                                                       (-40° C.)                                                                           20        22                                            Under Water-Absorbed Conditions                                                Tensile Strength                                                                          (23° C)                                                                             1000      900                                           (kg/cm.sup.2)                                                                  Flexural Modulus                                                                          (23° 40000     39000                                         (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg · cm/cm)                                                                     (23° C.)                                                                            28        30                                            Antifreeze Resistance (%)                                                                         90        85                                                ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon 66, nylon 6, polyethylene and modified          polyethylene are expressed by weight % based upon resin components, and        the content of glass fibers is expressed by weight % based upon the total      composition.                                                                   .sup.(2), (3), (6) Same as in Table 17.                                        .sup.(4) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.)                                                                   .sup.(5) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results in Tables 17 and 18, since the fiber-reinforced polymer compositions of the present invention not only contain the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also using nylon 66 and nylon 6 in the above proportion as the polyamide resins, they show remarkably improved impact resistance.

EXAMPLES 52-58

Nylon 46, nylon 66, nylon 6, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 19, and introduced into a double-screw extruder of 45 mm in inner diameter shown in FIG. 1 through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 19 into the double-screw extruder through its second hopper. They were blended at 300° C. to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 19.

                                      TABLE 19                                     __________________________________________________________________________                    Example No.                                                                    52    53    54    55    56    57    58                          __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 46.sup.(2)                                                                              30    50    60    30    30    5     0                           Nylon 66.sup.(3)                                                                              30    10    0     15    0     55    0                           Nylon 6.sup.(4)                                                                               0     0     0     15    30    0     60                          Polypropylene.sup.(5)                                                                         35    35    35    35    35    35    35                          Modified Polypropylene.sup.(6)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.2   0.2   0.2                         Content        5     5     5     5     5     5     5                           Glass Fiber.sup.(7)                                                                           35    35    35    35    35    35    35                          Molar Ratio of Amino Group/                                                                   17    15    14    18    19    20    23                          Carboxyl Group                                                                 Average size of                                                                               1.5   1     1     2     2     2     2                           Polypropylene Domain (μm)                                                   PROPERTIES                                                                     Thermal Deformation Temp.                                                                     260   270   280   255   250   240   190                         (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                        (23° C.)                                                                      2350  2350  2400  2000  1800  2300  1400                        (kg/cm.sup.2)                                                                           (140° C.)                                                                     1300  1400  1500  1300  1200  1100  550                         Flexural Modulus                                                                        (23°  C.)                                                                     83000 84000 85000 70000 65000 82000 50000                       (kg/cm.sup.2)                                                                           (140° C.)                                                                     40000 42000 50000 35000 30000 30000 10000                       Izod Impact Strength                                                           (kg · cm/cm)                                                                   (23° C.)                                                                      16    16    16    14    13    16    10                                   (-40° C.)                                                                     12    12    12    10    10    12    8                           Under Water-Absorbed Conditions                                                Tensile Strength                                                                        (23° C.)                                                                      1500  1500  1500  1500  1200  1500  1000                        (kg/cm.sup.2)                                                                  Flexural Modulus                                                                        (23° C.)                                                                      62000 62000 62000 57000 50000 61000 40000                       (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg · cm/cm)                                                                   (23° C.)                                                                      19    19    19    17    16    18    12                          Antifreeze Resistance (%)                                                                     85    85    85    85    60    85    60                          __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon 46, nylon 66, nylon 6, polypropylene and        modified polypropylene are expressed by weight % based upon resin              components, and the content of glass fibers is expressed by weight % base      upon the total composition.                                                    .sup.(2) Unitika Nylon 46 manufactured by Unitika Ltd. and containing end      amino groups in an amount of 0.026 milliequivalent/g measured according t      a KorshakZamyationa method (back titration method) (Chem. Abs. 40, 4665,       ♯, ibid 42. 6152, '48).                                            .sup.(3) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to the same KorshakZamyationa method as in (2).             .sup.(4) A1030BRT manufactured by Unitika Ltd. and containing end amino        groups in an amount of 0.042 milliequivalent/g measured according to the       same KorshakZamyationa method as in (2).                                       .sup.(5) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(6) Maleic anhydridemodified polypropylene.                               .sup.(7) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

EXAMPLES 59 AND 60

Fiber-reinforced polymer compositions were produced in proportions shown in Table 20 under the same conditions as in Examples 52 and 53 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above high-density polyethylene modified with carboxylic acids shown in Table 20 as the modified polyethylene, and the same measurements as in Examples 52 and 53 were conducted. The results are shown in Table 20.

                  TABLE 20                                                         ______________________________________                                                          Example No.                                                                    59      60                                                    ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 46.sup.(2)   30        60                                                Nylon 66.sup.(3)   30        0                                                 Nylon 6.sup.(4)    0         0                                                 Polyethylene.sup.(5)                                                                              35        35                                                Modified Polyethylene.sup.(6)                                                  Grafted Acid Content                                                                              0.2       0.2                                               Content            5         5                                                 Glass Fiber.sup.(7)                                                                               35        35                                                Molar Ratio of Amino Group/                                                                       17        14                                                Carboxyl Group                                                                 Average Size of    3         2.5                                               Polyethylene Domain (μm)                                                    PROPERTIES                                                                     Thermal Deformation Temp.                                                                         260       280                                               (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                          (23° C.)                                                                            2000      2100                                          (kg/cm.sup.2)                                                                             (140° C.)                                                                           1350      1400                                          Flexural Modulus                                                                          (23° C.)                                                                            80000     82000                                         (kg/cm.sup.2)                                                                             (140° C.)                                                                           38000     40000                                         Izod Impact Strength                                                           (kg · cm/cm)                                                                     (23° C.)                                                                            20        20                                                       (-40° C.)                                                                           18        18                                            Under Water-Absorbed Conditions                                                Tensile Strength                                                                          (23° C.)                                                                            1600      1700                                          (kg/cm.sup.2)                                                                  Flexural Modulus                                                                          (23° C.)                                                                            61000     63000                                         (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg · cm/cm)                                                                     (23° C.)                                                                            25        25                                            Antifreeze Resistance (%)                                                                         90        90                                                ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon 46, nylon 66, nylon 6, polyethylene and         modified polyethylene are expressed by weight % based upon resin               components, and the content of glass fibers is expressed by weight % base      upon the total composition.                                                    .sup.(2)-(4), (7) Same as in Table 19.                                         .sup.(5) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.).                                                                  .sup.(6) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results in Tables 19 and 20, since the fiber-reinforced polymer compositions of the present invention not only contain the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also using nylon 46 and if necessary, nylon 66 and/or nylon 6 as the polyamide resins, they show excellent mechanical strength, moldability, antifreeze resistance, etc., and their heat resistance and creep resistance are remarkably improved.

EXAMPLES 61-70

Nylon 12, nylon 612, nylon 11, nylon 66, nylon 6, polypropylene and modified polypropylene were dry-blended in a high-speed mixer in proportions shown in Table 21, and introduced into a double-screw extruder of 45 mm in inner diameter shown in FIG. 1 through its main hopper. The chopped strands of the glass fibers (average diameter: 13 μm, average length: 3 mm) were introduced in proportions shown in Table 21 into the double-screw extruder through its second hopper. They were blended at 230° C. (or 280° C. when nylon 66 or nylon 6 was contained) to provide composition pellets.

The resulting composition pellets were dried in a drying furnace and then injection-molded to provide test pieces to measure their properties. The results are shown in Table 21.

                                      TABLE 21                                     __________________________________________________________________________                    Example No.                                                                    61    62    63    64    65                                      __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 12.sup.(2)                                                                              30    50    60    30    30                                      Nylon 612.sup.(3)                                                                             0     0     0     0     0                                       Nylon 11.sup.(4)                                                                              0     0     0     0     0                                       Nylon 66.sup.(5)                                                                              30    10    0     15    0                                       Nylon.sup.(6)  0     0     0     15    30                                      Polypropylene.sup.(7)                                                                         35    35    35    35    35                                      Modified Polypropylene.sup.(8)                                                 Grafted Acid Content                                                                          0.2   0.2   0.2   0.2   0.2                                     Content        5     5     5     5     5                                       Glass Fiber.sup.(9)                                                                           35    35    35    35    35                                      Molar Ratio of Amino Group/                                                                   14    11    10    15    16                                      Carboxyl Group                                                                 Average Size of                                                                               1     0.8   0.7   1     1                                       Polypropylene Domain (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)                                                                            23    23    25    20    18                                      Thermal Deformation Temp.                                                                     230   190   180   205   200                                     (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                        (23° C.)                                                                      2000  1800  1800  2200  2000                                    (kg/cm.sup.2)                                                                           (140° C.)                                                                     1000  950   900   850   800                                     Flexural Modulus                                                                        (23° C.)                                                                      78000 70000 68000 70000 65000                                   (kg/cm.sup.2)                                                                           (140° C.)                                                                     26000 20000 18000 18000 12000                                   Izod Impact Strength                                                           (kg · cm/cm)                                                                   (23° C.)                                                                      16    17    18    16    16                                               (-40° C)                                                                      12    13    14    12    12                                      Under Water-Absorbed Conditions                                                Tensile Strength                                                                        (23° C.)                                                                      1800  1900  1800  1800  1800                                    (kg/cm.sup.2)                                                                  Flexural Modulus                                                                        (23° C.)                                                                      65000 68000 70000 65000 65000                                   (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           kg · cm/cm)                                                                    (23° C.)                                                                      17    17    17    17    17                                      Antifreeze Resistance (%)                                                                     90    90    90    85    85                                      __________________________________________________________________________                    Example No.                                                                    66    67    68    69    70                                      __________________________________________________________________________     COMPOSITION (wt. %).sup.(1)                                                    Nylon 12.sup.(2)                                                                              0     0     5     0     0                                       Nylon 612.sup.(3)                                                                             0     30    0     0     5                                       Nylon 11.sup.(4)                                                                              30    0     0     5     0                                       Nylon 66.sup.(5)                                                                              30    30    55    55    55                                      Nylon 6.sup.(6)                                                                               0     0     0     0     0                                       Polypropylene.sup.(7)                                                                         35    35    35    35    35                                      Modified Polypropylene.sup.(8)                                                 Grafted Acid Content                                                                          0.2   0.25  0.2   0.2   0.2                                     Content        5     5     5     5     5                                       Glass Fiber.sup.(9)                                                                           35    35    35    35    35                                      Molar Ratio of Amino Group/                                                                   16    18    20    20    20                                      Carboxyl Group                                                                 Average Size of                                                                               1     2     2     2     2                                       Polypropylene Doamin (μm)                                                   PROPERTIES                                                                     MFR (g/10 minutes)                                                                            25    25    14    14    14                                      Thermal Deformation Temp.                                                                     230   230   235   235   235                                     (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                        (23° C.)                                                                      2000  2000  2300  2300  2300                                    (kg/cm.sup.2)                                                                           (140° C.)                                                                     1000  1000  1100  1100  1100                                    Flexural Modulus                                                                        (23° C.)                                                                      80000 80000 82000 82000 82000                                   (kg/cm.sup.2)                                                                           (140° C.)                                                                     27000 27000 30000 30000 30000                                   Izod Impact Strength                                                           kg · cm/cm)                                                                    (23° C.)                                                                      16    16    16    16    16                                               (-40° C.)                                                                     12    12    12    12    12                                      Under Water-Absorbed Conditions                                                Tensile Strength                                                                        (23° C.)                                                                      1800  1800  1500  1500  1500                                    (kg/cm.sup.2)                                                                  Flexural Modulus                                                                        (23° C.)                                                                      65000 65000 61000 61000 61000                                   (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg ·  cm/cm)                                                                  (23° C.)                                                                      17    17    18    18    18                                      Antifreeze Resistance (%)                                                                     90    85    86    86    86                                      __________________________________________________________________________      Note:                                                                          .sup.(1) The contents of nylon 12, nylon 612, nylon 11, nylon 66, nylon 6      polypropylene and modified polypropylene are expressed by weight % based       upon resin components, and the content of glass fibers is expressed by         weight % based upon the total composition.                                     .sup.(2) Diamide L1600 manufactured by Daicel Huels Ltd. and containing        end amino groups in an amount of 0.017 milliequivalent/g measured              according to a KorshakZamyationa method (back titration method) (Chem.         Abs. 40, 4665, '46, ibid 42, 6152, '48).                                       .sup.(3) Diamide D14 manufactured by Daicel Huels Ltd. and containing end      amino groups in an amount of 0.028 milliequivalent/g measured according t      the same KorshakZamyationa method as in (2).                                   .sup.(4) Rilsan BMN manufactured by Toray Industries, Inc. and containing      end amino groups in an amount of 0.020 milliequivalent/g measured              according to the same KorshakZamyationa method as in (2).                      .sup.(5) Amiran CM 3001N manufactured by Toray Industries, Inc. and            containing end amino groups in an amount of 0.034 milliequivalent/g            measured according to the same KorshakZamyationa method as in (2).             .sup.(6) A1030BRT manufactured by Unitika Ltd. and containing end amino        groups in an amount of 0.042 milliequivalent/g measured according to the       same KorshakZamyationa method as in (2).                                       .sup.(7) J215 manufactured by Tonen Sekiyu Kagaku K.K.                         .sup.(8) Maleic anhydridemodified polypropylene.                               .sup.(9) MA03FT2 manufactured by Asahi Fiber Glass K.K.                  

EXAMPLES 71 AND 72

Fiber-reinforced polymer compositions were produced in proportions shown in Table 22 under the same conditions as in Examples 61 and 62 except for substituting high-density polyethylene (J-6311 manufactured by Tonen Sekiyu Kagaku K.K.) for polypropylene, and also using the above high-density polyethylene modified with carboxylic acids shown in Table 22 as the modified polyethylene, and the same measurements as in Examples 61 and 62 were conducted. The results are shown in Table 22.

                  TABLE 22                                                         ______________________________________                                                          Example No.                                                                    71      72                                                    ______________________________________                                         COMPOSITION (wt. %).sup.(1)                                                    Nylon 12.sup.(2)   30        0                                                 Nylon 612.sup.(3)  0         30                                                Nylon 11.sup.(4)   0         0                                                 Nylon 66.sup.(5)   30        30                                                Nylon 6.sup.(6)    0         0                                                 Polyethylene.sup.(7)                                                                              35        35                                                Modified Polyethylene.sup.(8)                                                  Grafted Acid Content                                                                              0.2       0.2                                               Content            5         5                                                 Glass Fiber.sup.(9)                                                                               35        35                                                Molar Ratio of Amino Group/                                                                       14        18                                                Carboxyl Group                                                                 Average Size of    2.5       3                                                 Polyethylene Domain (μm)                                                    PROPERTIES                                                                     MFR (g/10 minutes) 22        25                                                Thermal Deformation Temp.                                                                         225       230                                               (°C.)                                                                   Under Dry Conditions                                                           Tensile Strength                                                                          (23° C.)                                                                            1700      1700                                          (kg/cm.sup.2)                                                                             (140° C.)                                                                           800       800                                           Flexural Modulus                                                                          (23° C.)                                                                            65000     66000                                         (kg/cm.sup.2)                                                                             (140° C.)                                                                           20000     20000                                         Izod Impact Strength                                                           (kg · cm/cm)                                                                     (23° C.)                                                                            21        21                                                       (-40° C.)                                                                           18        18                                            Under Water-Absorbed Conditions                                                 Tensile Strength                                                                         (23° C.)                                                                            1700      1700                                          (kg/cm.sup.2)                                                                  Flexural Modulus                                                                          (23° C.)                                                                            60000     60000                                         (kg/cm.sup.2)                                                                  Izod Impact Strength                                                           (kg · cm/cm)                                                                     (23° C.)                                                                            21        21                                            Antifreeze Resistance (%)                                                                         90        90                                                ______________________________________                                          Note:                                                                          .sup.(1) The contents of nylon 12, nylon 612, nylon 11, nylon 66, nylon 6      polyethylene and modified polyethylene are expressed by weight % based         upon resin components, and the content of glass fibers is expressed by         weight % based upon the total composition.                                     .sup.(2)-(6), (9) Same as in Table 21.                                         .sup.(7) Highdensity polyethylene (J6311 manufactured by Tonen Sekiyu          Kagaku K.K.).                                                                  .sup.(8) Highdensity polyethylene (J6311) modified with maleic anhydride.

As is clear from the above results in Tables 21 and 22, since the fiber-reinforced polymer compositions of the present invention not only contain the unsaturated carboxylic acid-modified polypropylene or polyethylene serving to increase the compatibility of the polyamide resin and the polypropylene or polyethylene, but also using nylon 12, nylon 612 or nylon 11, and further nylon 66 and/or nylon 6, if necessary, they show excellent moldability, chemical resistance, antifreeze resistance, water absorption resistance, etc.

The fiber-reinforced polymer compositions of the present invention are highly suitable for containers such as radiator tanks of automobiles, parts disposed near automobile engines, parts of electric appliances, etc. 

What is claimed is:
 1. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin in a continuous matrix phase with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight %, and the molar ratio of end amino groups in said polyamide resin to carboxyl groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; and (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers.
 2. The fiber-reinforced polymer composition according to claim 1, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 3. The fiber-reinforced polymer composition according to claim 1 or 2, wherein said polyolefin is polypropylene, and said unsaturated carboxylic acid-modified polyolefin is unsaturated carboxylic acid-modified polypropylene.
 4. The fiber-reinforced polymer composition according to claim 1 or 2, wherein said polyolefin is polyethylene, and said unsaturated carboxylic acid-modified polyolefin is unsaturated carboxylic acid-modified polyethylene.
 5. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin in a continuous matrix phase with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight %, and the molar ratio of end amino groups in said polyamide resin to carboxyl groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; and (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers coated with a silane coupling agent and a tying agent of a polymer containing a carboxyl or acid anhydride group.
 6. The fiber-reinforced polymer composition according to claim 5, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 7. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin in a continuous matrix phase with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight % and the molar ratio of end amino groups in said polyamide resin to carboxyl groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers; and (d) 1-10 parts by weight, per 100 parts by weight of the total composition, of a spherical, flaky or fibrous inorganic filler.
 8. The fiber-reinforced polymer composition according to claim 7, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 9. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin in a continuous matrix phase with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxyl acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight %, and the molar ratio of end amino groups in said polyamide resin to carboxylic groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers; and (d) 0.03-3 parts by weight, per 100 parts by weight of the total composition, of at least one nucleating agent selected from the group consisting of a metal salt of an aromatic carboxylic acid, a metal salt of an alkyl group-substituted derivative of an aromatic carboxylic acid and dibenzylidene sorbitol.
 10. The fiber-reinforced polymer composition according to claim 9, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 11. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin consisting of nylon 66 and nylon 6 in a weight ratio of 40/60-90/10, said polyamide resin being in a continuous matrix phase, with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight % and the molar ratio of end amino groups in said polyamide resin to carboxyl groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; and (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers.
 12. The fiber-reinforced polymer composition according to claim 11, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 13. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin comprising nylon 46, said polyamide resin being in a continuous matrix phase, with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight % and the molar ratio of end amino groups in said polyamide resin to carboxylic groups in said unsaturated carboxyl acid-modified polyolefin is 10-1000; and (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers.
 14. The fiber-reinforced polymer composition according to claim 13, wherein said polyamide resin additionally contains at least one of nylon 66 and nylon 6 in a proportion of 85 parts by weight or less per 100 parts by weight of said polyamide resin.
 15. The fiber-reinforced polymer composition according to claim 13, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition.
 16. A fiber-reinforced polymer composition comprising a blend of (a) 50-70 weight % of a polyamide resin in a continuous matrix phase, wherein said polyamide comprises at least one of nylon 12, nylon 612 and nylon 11 with (b) 30-50 weight % of (i) a polyolefin having uniformly dispersed domain phases having an average size of 0.5-5 μm and (ii) an unsaturated carboxylic acid-modified polyolefin, wherein the amount of said modified polyolefin is 0.1-20 weight % and the molar ratio of end amino groups in said polyamide resin to carboxyl groups in said unsaturated carboxylic acid-modified polyolefin is 10-1000; and (c) 5-50 parts by weight, per 100 parts by weight of the total composition, of glass fibers.
 17. The fiber-reinforced polymer composition according to claim 16, wherein said polyamide resin further contains at least one of nylon 66 and nylon 6 in a proportion of 85 parts by weight or less per 100 parts by weight of said polyamide resin.
 18. The fiber-reinforced polymer composition according to claim 16, wherein (c) said glass fibers are 15-40 parts by weight per 100 parts by weight of the total composition. 